PLUGIN catalogue 2018

ERVAC Coaxial - general data Information source : HUBER+SUHNER RF Connector guide Plating materials Base materials Insulation materials 25 Properties Gold Silver Nickel SUCOPLATE® Density (g/cm 3 / lb/in 3 ) 18,0* 10,5 8,9 8,2 Melting at temperature °C / °F 1063 960 1453* na Electrical resistivity ϱ 20 (Ω mm²/m) 0,022 0,015 0,09 na Thermal conductivity (W/mK) 310 410 60 na Tensile strength at 20°C (N/mm² / 10 3 lb/in²) Elasticity mode (N/mm² / 10 6 lb/in²) 77 000 76 000 200 000 na Corrosion resistance ** ++ + + ++ Machinability ** ++ ++ na na Chemical resistance ** + + + ++ 120 140 320 na Brass Stainless steel Anticorodal (CuZn39Pb3) (303/1.4305) (AlMgSi1) Density (g/cm 3 / lb/in 3 ) 8,25 8,8 8,5 7,9 2,75 Melting at temperature °C / °F 865-980* 930-1060* 870-890 1420* 580-650 Electrical conductivity ( %IACS 20°C / 68°F ) Electrical resistivity ϱ 20 (Ω mm²/m) 0,083 0,087 na 0,73 0,039 na na na 115 80-85 120 Tensile strength at 20°C (N/mm² / 10 3 lbf/in²) 1270-1500* 350-820 380-590 500-750 310-370 Modulus of elasticity (N/mm² / 10 6 lbf/in²) +water, salt +water, salt water water +oil; 0 acids -to with acids base; bases -ammoniums & ammoniums Machinability ** + na ++ + ++ Corrosion resistance ** 0 + ++ Chemical resistance ** + 0 ++ Thermal conductivity (W/mK) 130 000 118 000 96 000 200 000 70 000 15 170 12* 11,5* 16 na na Properties Beryllium Copper (CuBe) Bronze Properties PE (PE-HD) PTFE PFA FEP PEEK PPO Density (g/cm 3 / lb/in 3 ) 0,94 2,16 * 2,15 2,16 * 1,3 1,06 Temperature range °C / °F -50 - +70 -200 - +260 -200 - +260 -100 - +200 -70 - +250 -30 - +140 Melting at temperature °C / °F 130 327 305 225 334 230 Dielectric constant at 1 MHz 2,3 2,1 2,1 2,1 3,3 2,7 Electrical resistivity (Ω mm²/m) > 1 x 10 17 > 1 x 10 18 > 1 x 10 17 > 1 x 10 18 > 1 x 10 16 > 1 x 10 17 Tensile strength at 20°C (N/mm² / 10 3 lb/in²) Modulus of elasticity (N/mm² / 10 6 lbf/in²) Water resistance (at 23°C / 73°F) Flammability ** HB-V-O V-O V-O V-O V-O na Chemical resistance ** + ++ ++ ++ ++ na * Owing to di erences in purity in the case of elements and of composition in metals, the values can be considered only as approximations ** The abilities of the materials (to be treated, shaped, etc.) are rated from ++ (excellent), + (good), 0 (fair), - (poor) to - - (very poor) compared with each other 92,0 60,0 * 790 - 1000 460 na 350 3900 + 27 27 26 20 2500 ++ - ++ ++ +